D2I工具钢是一种高碳高铬的空气硬化工具钢，可以进行热处理以达到高硬度和高抗压性。D2工具钢具有出色的耐度性，广泛用于需要边缘锋利、耐磨性、高 抗压性的冷加工应用中。Markforged D2符合ASTM A681的化学要求。
MATERIAL DATASHEET
D2 Tool Steel
Composition | Amount |
Chromium | 11-13% |
Carbon | 1.4-1.6% |
Molybdenum | 0.7-1.2% |
Vanadium | 0.5-1.1% |
Nickel + Copper | 0.75% max |
Manganese | 0.10.6% |
Silicon | 0.1-o.e% |
Phosphorus | 0.03% max |
Sulfur | 0.03% max |
Iron | bal |
Typical Mechanical Properties | Standard | Markforged As-Sintered | Markforged Heat-Treated1 | Wrought Heat Treated2 |
0.2% Compressive Yield Strength | ASTM E9 | 830 MPa | 1690 MPa | 2200 MPa |
Elastic Modulus | ASTME9 | 170 GPa | 187 GPa | 210 GPa |
Hardness3 | ASTM E18 | 54 HRC | 60 HRC | 62 HRC |
Relative Density4 | ASTMB923 | 97% | 97% | 99% |
D2工具钢在退火步步骤和加工后，可通过热处理以提高硬度和耐用性。Markforged建议对D2工具钢进行热处理，以优化材料性能。
1.在标（非真空）炉中将D2工具钢零件加热到1000°C (1830oF),保持30-40分钟。
2.将零件空气淬火至低于65°C <150°F).
3.在标准炉中回火D2工具钢零件。对于毎种回火，将零件加热到200°C5 (392oF),回火30分钟。如果要双重回火在回火之间让零件冷却至室温。